Undoped PbTiO3 ceramics was successfully prepared by using sol-gel process, which had not been fabricated due to its microcracks created by anisotropic stress during phase transition from cubic to tetragonal phase. Fabrication of undoped PbTiO3 ceramics via sol-gel processing was very much affected by the PbO content of the samples as well as PbO vapor from sintering atmosphere. Excess PbO was found to promote rapid grain growth in PbTiO3 ceramics. After sintering at 1100$^{circ}C$ average grain size of PbTiO3 ceramics with excess PbO was about 8 times greater than that of stoichiometric composition, which may be due to PbO liquid phase from excess PbO.