The effects of CaO addition on the low temperature degradation behavior of 2.5Y-TZP ceramics were investigated. Y2O3-CaO-ZrO2 ceramics were prepared from the commercial Y-TZP powder added within 1 mol% of CaO. Fully tetragonal phase could be obtained at each composition under sintering condition of 1500$^{circ}C$ for 1 hour. As the amount of CaO increased, grain size was decreased. From the result of heat treatment at 200$^{circ}C$, volume fraction of monoclinic phase formed on the surface of each specimen was decreased with higher CaO amount. Stability of tetragonal ZrO2 phase for low temperature heat treatment was increased by CaO addition without the degradation of mechanical properties.