SiC and Si mixtures dispersed by 0.5~10.0 wt% of Al2O3 and reinforced by SiC whisker were sintered to Si3N4 bonded SiC bodies at 140$0^{circ}C$ in a N2 gas atmosphere, and the nitridation and mechanical properties of sintered bodies were investigated. From these observation, it is concluded that relative density and bending strength increased with the rising of nitridation and the highest nitridation ratio was obtained for a specimen having 1.5 wt% Al2O3. On the other hand, the amount of $eta$-Si3N4 in the specimens containing Al2O3 more than 5.0 wt% was increased abruptly and the best in fracture toughness was sintered for a composits having 30 wt% SiC whiskers.