The purpose of this study was to describe the heterogeneity effects on Intermediate/Final microstructure in isothermal liquid phase sintering. Several kinds of pore shapes were made by the different in the heterogeneity stress level during Intermediate/Final stage. Specimen with 48% green density especially showed that the local regions of a sintered compact were subject to more rapid shrinkage than the surroundings. This densification limiting factors generally inhibited sintering and made the large isolated crack-like pore in heterogeneous microstructures.