Weathering of wood in a region of acid rain was performed by the test which thin veneers of Sitka spruce were exposed to outdoor weathering for a total of 18 weeks, with a daily soaking for 30 minutes in acidified water in the pH range 2~5.6. The weathering measured by weight loss and loss in maximum failure load in tension was accelerated by the increase in the acidity of acidified water and in the period of outdoor exposure. It was also shown that the weathering was accelerated even with low acidic conditions in the case of long exposure period, although the weathering was rapidly accelerated with high acidic conditions. When compared the degree of weight loss with that of loss in failure load by weathering, the latter was much greater. From the results of this research, it could be concluded that at pH 4.0 or below of precipitation, the acceleration of weathering of exterior wood would become serious problems, which would be caused deterioration in performance of exterior wood.