This study was carried out to investigate the fracture criterion of glulam. The mixed mode fracture of glulam was investigated by means of single edge notched specimens with various crack inclination in the longitudinal-radial plane. While fracture of wood is not completely understood, the study on linear-elastic fracture mechanics is a rational and valuable tool for studying the strength behavior of glulam. The results are summarized as follows : 1. Glue line has no effect on fracture strength. 2. There is a definite interaction between fracture toughness $K_I$ and $K_{II}$ during the mixed mode fracture of glulam. Several criterions for mixed mode failure were compared. The criterion was expressed in the following form: $(frac{K_I}{K_{IC}})^2+(frac{K_{II}}{K_{IIC}})^2=1$ 3. As crack inclination increases, $K_{IC}$ value and $K_{IIC}$ value decreases. The equations relating crack angle to $K_{IC}$ and $K_{IIC}$, respectively, were obtained as follows; $K_{IC}$ = -77.42${gamma}$+153.72 ($R^2$ = 0.78) $K_{IIC}$ = -9.17${gamma}$+34.90 ($R^2$ = 0.48)