Dental abrasive, dicalcium phosphate dehydrate (DCPD) was prepared and the several important factors affecting on the quality of toothpaste were investigated by means of set test, glycerine absorption, Coulter counter test, color difference, BET adsorption, mercury porosimetery, and rheogram comparing with two foreign DCPDs, MFO4 and Dentphos K. Sample DCPD was prepared by reaction between 85% H$_{3}$PO$_{4}$ and 15% milk of lime at $39^{circ}C$ (pH6.5), and stabilized with TSPP and TMP. The physicochemical properties of Sample DCPD were obtained as follows: whiteness (98.99), average particle size (15.5 $mu extrm{m}$), pH (7.9), remainder particle weight (0.49w/w%), glycerine absorption value (64 ml), and set test (passed). N$_{2}$ adsorption curves (BET) of three kinds of DCPD showed non-porous type III isotherm. BET adsorption parameters of sample DCPD showed that surface area was 24.9 m$^{2}$/g, total pore volume 0.09 cm$^{3}$/g and average pore radius 72.0 $AA$. The rheogram of the toothpaste containing each DCPD showed bulged plastic flow with yield vlaue and thixotropic behavior. These results meet standard requirements as abrasive standard, and suggested that synthesized sample DCPD could be used a dental abrasive such as a high quality grade in practice as foreign DCPDs.