The effects of MgO addition on thermal expansiion coefficient and dielectric constant of mullite were studied. Thermal coefficient and dielectric constant decrease with increasing MgO content and exhibit a minimum value at 1wt% MgO. However, above 3wt% MgO content both values increase. Result of X-ray diffraction analysis how that mullite compositions which include more than 0.1wt% MgO form cordierite. Spinel is also formed as well as cordierite in the composition containing more than 3wt% MgO. The results indicate that addition of MgO affect the thermal expansion coefficient and dielectric constant of mullite substrate because of the formation of new phases; cordierite and spinel. The thermal expansion coefficient and dielectric constant are affected mainly by cordierite and spinel in the regions containing less than more than 3wt% MgO, respectively.