The purpose of this study was to observe the resin infiltration pattern into dentin by various dentin bonding agents. Freshley extracted 36 sound human molars were used in this study. They were stored at $4^{circ}C$ physiologic saline solution before experiment. All the teeth were cross-sectioned to expose dentin below about 3.0mm at the cusp tip and above 2.0mm at the cemento-enamel junction with Crystal Cutter (MC411 D, Maruto Co., Japan), and were made into specimens for this study (Fig. 1). The specimen experimental groups were divided into 9 groups by dentin surface treatment as following procedures: Group I: Treated with Gluma Cleanser followed by Gluma Primer and Sealer Group 2. Treated with Gluma Cleanser followed by Scotch bond 2 Adhesive Group 3: Treated with Gluma Cleanser followed by Tenure Solution A, Band Visar Seal Group 4: Treated with Scotchprep followed by Scotch bond 2 Adhesive Group 5: Treated with Scotchprep followed by Gluma Primer and Sealer Group 6: Treated with Scotch prep followed by Tenure Solution A, Band Visar Seal Group 7: Treated with Tenure Conditioner followed by Tenure Solution A, Band Visar Seal Group 8: Treated with Tenure Conditioner followed by Scotchbond 2 Adhesive Group 9: Treated with Tenure Conditioner followed by Gluma Primer and Sealer 27 specimens of 36 specimens were divided into 9 groups (Group 1-9), and were used for observation of resin tags. Remaining 9 specimens were divided into 3 groups (Group 1,4 and 7), and were used for observation of fractured dentin surfaces. Specimens to observe the resin tag were demineralized with 20% HCl for 14 hours, specimens to observe the fractured dentin surfaces were demineralized with 10% HCl for 3 minutes. All the specimens were gold-coated with Eiko ion coater (Eiko-engineering Co.), and observed under Scanning electron microscope (Hitachi S-2300) at 20 KV. The following results were obtained: 1. In group 1 treated with Gluma Cleanser, Gluma Primer, and Sealer, most resin tags were more than $100{mu}m$. 2. In group 4 treated with Scotch prep and Scotchbond 2 Adhesive, most resin tags were about $10{mu}m$. 3. In group 7 treated with Tenure conditioner, Tenure Solution A, B, and Visar Seal, most resin tags were about $10{mu}m$ but occasionally resin tags were more than $100{mu}m$. 4. In groups 2,3,5,6,8 and 9, the lengths of resin tags were inconsistent and the amount of resin tags were reduced.