YBa2Cu3Ox-Ag(YBCO-Ag) thick films were fabricated on the zirconia substrate by a screen printing method. The starting powder was a mixture of YBCO, prepared by a coprecipitation in oxalic acid, and Ag2O. The influence of heat treatment conditions on properties of thick films was investigated. It was observed that Jc of thick films was directly proportional to the orientation factor of thick films and the optimimum preparation condition was the heat treatment of thick films at 100$0^{circ}C$ for 3 min in O2. The improvement of Jc by the addition of Ag was considered as a result of the suppression of microcracks in the films.