The magnetic properties of aluminum anodized film in which Co-Fe alloy electrodeposited are investigated with regard to the alloy composition of magnetic films. The electrodeposited Co-Fe particles are confirmed to be single phase Co-Fe alloys by X-ray diffractions. At 34 at% Co, the sample with small pore diameter(particle diameter $150;{AA}$) has a large magnetic energy product($B_{max}$) of about 1.44 MGOe due to the large saturation magnetization, the high coercive force and good squareness of the M-H curve. However, for the samples with particle diameter larger than $450;{AA}$, the bottom of each particle forms abnormal particle claaed branch-shaped unlike the sample of the particle diameter $150;{AA}$. In this case, the magnetic anisotropy energy was about zero at the compositions of 45 and 75 at% Co. Moreover, at the compositions from 50 to 70 at% Co, the anisotropy became negative value. This means that an easy axis of magnetization of the film is in plane in plane in spite of the perpendicular shape anisotropy of the particle. It was found that the bottom extremity of the particle contains FeC from the X-ray diffraction. Thus the effect of the bottom extremity, that is, an unusal magnetic property was removed by electrodepositing Cu at the bottom extremity of the particle. Itis clear that the magnetic properties of the ilms are influenced by he branch-shaped bottom extremity filled with FeC.