We have investigated the effects of sputtering Ar gas pressure on magnetic and magneto-optical properties in compositionally modulated Co/Pt superlattice thin films. The samples were prepared by dc magnetron sputtering. Sputtrering Ar gas pressure was varied from 2 to 30 mTorr. The microstructure of the samples was examined by scanning electron microscope and the x-ray diffractometry. The magnetization, the Kerr rotation angle, and the reflectivity of the samples were measured. The columnar structure was developed, and the coercivity was drasti- cally increased, when the sputtering Ar gas pressure was higher than 20 mTorr. We explained that the variation of the magnetization, the Kerr rotation angle, and the reflectivity was related with the microstructure influenced by the variation of the Ar gas pressure.