Metallizing method on ceramic surface is one of the compositing technology of ceramics and metal. The purpose of this study is to make HIC (Hybrid Intergrated Circuit) with copper metallizing method of which copper layer is formed on ceramic substrate by firing in atmosphere in lieu of conventional hybrid microcircuit systems based on noble metal. Metallizing pastes were made from various copper compounds such as Cu$_{2}$O, CuO, Cu, CuS and kaolin. And the screen printing method was used. The characteristics of metallized copper layers were analyzed through the measurement of sheet resistance, SEM, and EDZX. The results obtainted are summarized as follows; 1. The copper metallizing layers on ceramic surface can be formed by firing in air. 2. The metallized layer using Cu$_{2}$O paste showed the smallest sheet resistance among a group of copper chemical compounds. And optimum metallizing conditions are 15 minutes of firing time, 1000.deg.C of firig temperature, and 3 minutes of deoxidation time. 3. The results of EDAX analysis showed mutual diffusion of Cu and Al. 4. The kaolin plays a important role of deepening the penetration of Cu to $Al_{2}$O$_{3}$ ceramics. But if the kaolin content is too much, sheet resistance increases and copper metallizing layer becomes brittle.