Weldability of DS100 and HY type high strength-toughness steel plates, tentatively produced as domestic production, was investigated. DS100 and DS130A had nearly same hardenability in HAZ in spite of its difference in Ceq. Based upon the y-groove test results, cold cracking susceptibility of DS130 was superior to that of DS100 because of its lower hydrogen level in weld metal. Solidification cracking tested by the Trans-Varestraint test was occured in all of the weld metals, and its susceptibility was high in the row of DS100, DS130A and DS130B. However, no liquation cracking and ductility-dip cracking tested by the Longi-Varestraint test with 6.0% augmented strain were detected in base metal and reheated weld metal. Toughness in the GMA welding joint was satisfied with the relative Mill Spec, even though welded joint of DS100 had relatively low impact energy especially at the weld metal.