A study was carried out for the development of direct determination of antimony in high purity copper metal without preseparation. The large excess of copper seemed to be performed as the matrix modifier to enhance the absorbance of antimony in copper metal. Sensitivity enhancement of Sb was obtained at the condition of the ashing temperature of $600^{circ}C(20s){sim}700^{circ}C(10s)$ rather than $1000^{circ}C(20s){sim}1100^{circ}C(10s)$, and the atomization temperature of $2200^{circ}C.$ The operating pressure of argon gas was readjusted to the optimum condition at 2.0 kg/$cm^2.$ The linearity of the Sb calibration graph could be obtained in the range of 20 ppb up to 200 ppb Sb in existence of 5,000 ppm Cu with the coefficient of variation of about 5%.