In this study, we have analyzed structural analysis and measured ferroelectric characteristics of PZT thin films prepared by sol gel process with different sintering conditions and different Zr/Ti mot%. When the Zr mot% of PZT thin film was increased, it was found that the remanent. polarization and coercive field were decreased and increased, respectively. Also, the maxium dielectric constant of PZT(50/50) thin film was 786.8. We got double hysteresis(anti-fcrroelectric) curve from PbZrO$_{3}$ thin film. As heating rate goes up, pyrochlore phase of PZT thin film was decreased and dielectric and ferroelectric characteristics were improved. As a result of variation of sintering temperature and time 500.deg. C-800.deg. C and 5 sec.-8 hours, respectively, we got optimal sintering temperature and time. The optimium sintering temperature and time of conventional furnace method and rapid thermal processing method were 650.deg. C-700.deg. C for 30-60 minutes and 700.deg. C/20 seconds-2 minutes, respectively.