In a recent investigation, the formation of bainite phase in direct-quenched low carbon non heat-treated steel was reported. In this study the effects of bainite phase on the mechanical properties of direct-quenched microalloying steels were investigated. By isothermal transformation at $480^{circ}C$ for 7 sec., volume fraction of bainite lath was 15~20%, and the UTS and impact energy were increased. In this case $B_{ll}$ and $B_{lll}$ type bainite was observed and the fractography of impact test specimen showed a ductile fracture tendency. Isothermal transformation for 100sec., yielded 30% volume fraction of granular bainite and the mechanical properties were decreased. The f ractography of impact test specimen showed a brittle fracture tendency. The addition of Mo was more effective than B for improving impact energy because amounts of boron aditions were restricted to considerably lower levels, typically 10~ 30ppm. From this study, it is predicted that 15~20% volume fraction of lath bainite on the direct quenching process is procduced by addition of Mo up to 1.2wt. % and controlling the finish forging proc¬ess at $1000^{circ}C$ and using oil as direct quenching media. This will improve mechanical properties of the direct- quenched steel.