A rf reactive sputter deposition technique was adopted to deposit ferroelectric lead zirconate titanate (PZT) thin films with high rate from a ZrTi alloy target combined with PbO pellets. Deposition characterisitics including the effects of PbO are ratio were discussed. A new deposition mode called the quasi-metallic mode was observed. Perovskite PZT films were prepared at a growth temperature as low as$ 450^{circ}C$. However, because the target structure is unstable, weproposed a mixture target consisted of Zr, Ti and PbO. Fundamental experiments were investigated using the powder target. Perovskite PZT film could be obtained at $450^{circ}C$ with better electrical properties also.