The electrical and electromagnetic shielding properties have been investigated in polyaniline free standing films with different degrees of elongation cast from N-methyl 2-pyrrolidone(NMP) solution and camphorsulfonic acid(HCSA) doped polyaniline film. The degree of crystallinity of the crosslinked films increased with increasing the draw ratio. For the case of the oriented films doped with hydrochloric acid, we have the values of conductivities up to 173 S/cm. It is considered that the physical micro-crystalline crosslinking domains act as nucleation sites for the increase of relative crystallinity during stretching. We have obtained the value of conductivity 210 S/cm in the HCSA doped polyaniline film cast from the solvent of m-cresol, which is higher than that of the crosslinking oriented films. The electromagnetic shielding efficiency of HCSA doped polyaniline film obtained 37-41 dB in the frequency range of 10MHz-1GHlz, which is higher than that of the crosslinking oriented films. The higher value of electromagnetic shielding efficiency of HCSA doped polyaniline film suggests strong possibility of electromagnetic shielding material.