TiN and AlN are ceramic materials with extensive applications due to its excellent mechanical and chemical properties at elevated temperature. The purpose of this research is to develop the method for the synthesis of ternary nitride powder, titanium-aluminum-nitrogen system, which have an excellent property of both TiN and AlN. The ternary nitride such as $Ti_3AlN$, $Ti_2AlN$ and $Ti_3Al_2N_2$ can be synthesized by the interdiffusion nitriding method in Ar gas, however, the ternary nitride coexist with TiN, AlN, $Ti_3Al$ and ${alpha}$-Ti. The ternary nitride are stable below $1400^{circ}C$, but these are gradually decomposed into TiN, $Ti_3Al$ and AlN above $1400^{circ}C$. The thermal oxidation characteristics of the Ti-Al-N compound synthesized by the interdiffusion nitriding method is superior to that of the TiN+AlN mixed powder, and the oxidation for both materials show the differential behaviors.