The effect of variation of pack activators, compositions, temperature and time on the thickness and structure of aluminide coatings formed on the TiAl alloy was studied in one-step packs and two-step packs containing aluminum for the purpose of improvement of oxidation resistance. The thickness of coating layer was increased with increasing $NH_4Cl$ content up to 3wt% and then it was saturated. Oxidation resistance of coating layers carried out at one step pack was superior to that of ones through of two step pack. The improvement of high temperature oxidation resistance was due to the formation of a protective $Al_2O_3$ surface layers and coating the alloys with $TiAl_3$ phase.