Amorphous (Ba, Sr)$TiO_3$[BST] layer(30, 70 nm) was introduced between crystalline BST and $RuO_2$electrode to realize double-layered BST structure in order to improve the properties of BST film. The structure and surface morphology of double-layered BST film were modified by the application of amorphous BST layer; that is, surface became smoother and grain size increased abruptly. Amorphous layer thicker than 30 nm was effective to hinder the influence of $RuO_2$surface on the structure of as-grown BST films by in-situ process. Dielectric constant of double-layered BST film was improved dramatically from 152 to 340 and leakage current was lowered from $1.25{ imes}10^{-5}A/{ extrm}{cm}^2);to;6.85{ imes}10^{-7}A/{ extrm}{cm}^2$, respectively.