Densification and grain growth behaviors of ITO ceramics were investigated as a function of TiO2 ad-ditions. TiO2 addition led to inhibition of the grain growth and promotion of the densification of ITO ceram-ics. From the microstructure observation it was found that the crack-like voids which were formed in pure ITO specimens decreased with increase of TiO2 additon. The grain growth exponent(n) was measur-ed to be 4 for pure ITO 3 for TiO2-doped ITO specimens respectively. It was supposed that the grain boun-dary migration of pure ITO ceramics was controlled by the pores which were moved by surface diffusion. On the contrary the grain boundary migration of TiO2-doped ITO specimens was depressed by solute drag effect. The activation energies for grain growth were measured to be 1013 kJ/mol for pure ITO ceramics and 460kJ/mol for TiO2-doped ITO specimens respectively.