We smelted thc pellets made by mixing the distilled carbon from wlISte Lires, LD converter dust and slag with reduction process in the revcrberatory furnace. Thc obtained results are as follows 1) The removal mte of zinc appears above 97% after T reducing the pellets at $1300^{circ}C$ for Ihr and the zinc content in the residue are 0.1~D.2%. 2) Under the mixing condition of 500 g LD dust. 150-200 g LD slag and 30-50 g distilled carbon of waste lires the removal raho of zinc shows above 95%, while t the 50-60% Fe remains in the residue. 3) After smelting at $1350^{circ}C$ for 3hrs, the recovery ratio of pig iron reduced from lhe p pellets containing 15-20% LD slag and 4.1-7.2% distilled carbon of waste tires appears in the range of 89.3-92%. 4) Tbe c chemical composition of the recovered pig iron is 1.7%C, O.05%P, 0.05%S and balance Fe. 5) Tbe recovered dust from the d dust collcctor alter finishing the reduction rcaction appears as a crude zinc oxide conLaining 60% zinc.