In this paper, the optical properties of boron ion implanted GaAs were investigated by photoluminescence(PL) measurements. The implantations were preformed at room temperature with the energy of 150 eV. The range of implanted dose was $10^{12}~10^{15} ions/cm^2$. The boron implanted samples were annealed between $450^{circ}C$ and $800^{circ}C$ for 20 minutes. The crystallinity of low dosed samples were increased with increasing annealing temperature up to $700^{circ}C$ while that of the high dosed($10^{15} ions/cm^2$) was almost same. From the samples with dose of $10^{14}~10^{15} ions/cm^2$, two emission bands were observed at 1.438 eV (B1) and 1.459 eV (B2) after the thermal treatment. These emission bands seems to be attributed to the $B_{Ga}$-defect complex.