The objective of this paper is to provide experimental data of Er(rare- earth)doped $SiO_2$thin film made by sputtering methods. The deposition rate of silica glass by sputtering method was 55$AA$/min. In EDD measurements, the average Er concentration in the deposited film was 0.77(wt%). After annealing at $900^{circ}C$, the Cl concentration decreased from 3.79(wt%) to 1.52(wt%). The refractive indices of the core $n_1$, cladding $n_2$ were 1.458, 1.558 respectively at 632.8 nm. The refractive index difference between core and cladding, $Delta$n was 0.1. The refractive index profile of core and cladding interface shows step profile. In the study, $SiO_2$ glass films of Si wafer were successfully doped with active erbium. Therefore, this experimental data will be applicable for fabrications of Er doped planar integrated optical device.