The purpose of this study was to determine the effect of bleaching technique on the shear bond strength of esthetic restorative materials to bovine enamel. The bleaching agent was used 35% $H_2O_2$(Hi-Lite, Shofu, U.S.A.). Experimental groups were divided into two divisions as group A and B. Experimental A groups for the effect of number of bleaching were as follows ; Group Al : no bleaching Group A2 : bleaching 1 time ( for 5 minutes ) Group A3 : bleaching 3 times ( each for 5 minutes ) Group A4 : bleaching 6 times ( each for 5 minutes ) Group A5 : bleaching 9 times ( each for 5 minutes ) Experimental B groups for the effect of storage period in artificial saliva were as follows ; Group B1 : not stored in artificial saliva after bleaching Group B2 : stored in artificial saliva for 1 day after bleaching Group B3 : stored in artificial saliva for 1 week after bleaching Group B4 : stored in artificial saliva for 2 weeks after bleaching Group B5 : stored in artificial saliva for 4 weeks after bleaching Composite resin and glass ionomer cement were bonded to all specimens, and the shear bond strength between enamel and r~storative material were measured in Instron Universal Testing Machine(Instron, 4467, U.S.A,), Additionally, the bleached enamel specimens were examed after etching with 37.4% $H_3PO_4$ for 1 min under SEM(S-2300, Hitachi Co., Japan) to observe the effect of bleaching procedure on enamel surface morphology. The result were as follows ; 1. In SEM findings, bleached bovine enamel was found to be superficially rough. 2. In bleached bovine enamel, the effect of acid etching was reduced with the increase of number of bleaching. 3. The mean shear bond strength of composite resin and glass ionomer cement to bleached enamel surface tended to be lower than those to non-bleached enamel surface. 4. With the increase of number of bleaching, the shear bond strength of composite resin and glass ionomer cement to bleached enamel were progressively decreased. 5. Increasing the, storage period in artificial saliva after bleaching, the shear bond strength of composite resin and glass ionomer cement to bleached enamel were progressively increased. 6. The mean shear bond strength of glass ionomer cement to bleached bovine enamel tended to be clearly lower than that of composite resin.