The purpose of this study was to evaluate the effects of fluoride application on the aspect of shear bond strength of three aesthetic restorative materials to dentin. One light-cured composite resin(Palfique Esterite) and two light-cured glass ionomer cements(Fuji II LC and Compoglass)were used in this study. 120 permanent molars were used for this study. The teeth were extracted due to the origin of periodontal disease. The crowns of all teeth were removed, and the remaining roots were embedded in epoxy resin. The mesial or distal surfaces of roots were ground flat to expose dentin and polished on wet 320-, 400-, and 600 grit SIC papers for a total of 120 prepared flat root dentin surfaces. The prepared samples were divided into six groups. Group 1, 3, and 5 were control groups and group 2, 4, and 6 were experimental groups. Sixty samples for experimental groups were treated with 2% NaF solution for 5 minutes. Group 1 and 2 were bonded with Plafique Esterite, group 3 and 4 were bonded with Fuji II LC, and group 5 and 6 were bonded with Compoglass. After 24 hours water storage at $37{pm}1^{circ}C$, all samples were subjected to a shear to fracture with Instron universal testing machine(No.4467) at 1.0 mm/min displacement rate. Dentin surfaces treated with each conditioners before bonding and interfacial layers between dentin and aesthetic restorative materials were observed under Scanning Electron Microscope(Hitachi S-2300) at 20Kvp. The data were evaluated statistically at the 95% confidence level with ANOVA test. The result were as follows; 1. Among the control groups, group 1 showed strongest bond strength and group 3 showed weakest. 2. Among the experimental groups, group 2 showed strongest bond strength and group 6 showed weakest. 3. Statistical analysis of the data showed that pretreatment of dentin with 2% NaF solution significantly decreased the bond strength of three aesthetic restorative materials to dentin(P<0.05). 4. SEM findings of fluoride treated dentin surfaces (2, 4, 6 group) demonstrated dentin surfaces covered with fluoridated reaction products. 5. Except group 4 and 6, resin tags were formed in all groups.