Behaviors of abnormal expansion during calcination process of Ba2Ti9O20 ceramics and its related effects on the sintering characteristics were investigated as a function of precursors. When BaCO3 and TiO2 powders were used as starting materials. BaTi4O9 phase which has relatively large molar volume was formed drastically with abnormal ex-pansion during the calcination at 95$0^{circ}C$ to 115$0^{circ}C$ ON the contrary using BaTiO3 and TiO2 powders as starting materials led to retardation of the formation of BaTi4O9 phase and concurrently suppressed the abnormal expansion during cal-cination process. Especially the calcined powder of BaTiO3 and TiO2 had advantages in the densification and formation of Ba2Ti9O20 single phase in the sintering process.