The electrical conductivity ($sigma$) of TiO2 doped with 0.05-4.0mol% Nb2O5 was measured in the oxygen partial pressure range of 10-17 to 100 atm and temperature range of 1100 to 130$0^{circ}C$ to investigate the electrical properties and defect types. The oxygen partial pressure dependence of the electrical conductivity (log$sigma$/logPo2) above 110$0^{circ}C$ was divided into the four regions. From these experimental results the following defect regions were proposed ; 1) Magneli phase(extended defect) 2) reduced rutile region where intrinsic defect predominates 3) nearly stoichiometric region which is independent on the oxygen partical pressure and 4) overstoichiometric region which is not observed in pure TiO2 The electrical conductivity of Nb-doped TiO2 depended on the doping content the oxygen partial pressure and the measuring tem-perature.