The $BaTiO_3$ powders were synthesized by GNP (Glycine-Nitrate process). The powders were prepared using carbonate and alkoxide as starting materials and nitric acid was used as a solvent for starting materials as well as an oxidant for combustion. the effects of aggregates in $BaTiO_3$ powders on green densities, sintering and dielectric characteristics were investigated. When the glycine/cation molar ratio was 1.2, reactivity of self-combustion was most intensive and the degree of aggregates after calcination was low. On sintering at $1400^{circ}C$, maximum theoretical relative density(94.99%%0 was obtained in case of 1.2 molar ratio of glycine/cation. The dielectric constant of this sintered $BaTiO_3$ was 1919.