Hydrogenated amorphous silicon (a-Si:H) films are fabricated by Argon radical annealing (ArRA). The deposition rate of continuously deposited a-Si:H film is 1.9 $AA$/s. As ArRA time are increased to 0.5 and 1 minute, the deposition rate are increased to 2.8 $AA$/s and 3.3 $\AA$/s. The deposition rate of a-si:H films with 2 and 3 minutes ArRA time are 3.3 $AA$/s. As the ArRA time is increased, the optical band gap and the hydrogen contents in the a-Si:H films are increased and slightly decreased. The light-induced degradation of ArRA treated a-Si:H films are less than that of continuously deposited a-Si:H film. The dark conductivity and the conductivity activation energy ($E_a$) of continuously deposited a-Si:H film are decreased to 1/25 in room temperature and increased to 0.09eV By 1 hour light soaking, respectively. The dark conductivity and $E_a$ of ArRA treated a-Si:H film decreased to 1/3 in room temperature and increased to 0.03eV by 1 hour light soaking, respectively. We could improve the stability of a-Si:H films under the light soaking by ArRA technique and discussed the microscopic process of ArRA technique.