The electrical properties due to mixture ratio of linear low density polyethylene(LLDPE) and ethylene vinyl acetate(EVA) films are studied. An experimental specimen is selected as LLDPE/EVA of thickness 200${mu}{ extrm}{m}$ produced by mixture ratio of 50 : 50, 60 : 40, 70 : 30 and 80 : 2 wt%. In temperature range from $25^{circ}C$ to 12$0^{circ}C$, the measurement of volume resistivity using a highmegohm meter is performed within 10 minutes since each voltage of DC 100 V, 250 V, 500 V and 1000 V is applied, according to the step voltage method. From FT-IR spectrum for an analysis of physical properties, it can be confirmed that LLDPE blended with EVA shows an absence of carbonyl groups(1735 $cm^{-1}$, C=0) and ether groups(1242 $cm^{-1}$, C-O). The peak of LLDPE and EVA made of mixture ratio of 70 : 30 at 2$ heta$ =21.4$^{circ}$ in the results of XRD is higher than the others. In the experiment for volume resistivity characteristics in order to investigate the electrical properties of specimen, it is confirmed that volume resistivity is decreased with the increase of the molecular motion and temperature.