PZT(53/47) precursor 1M sols were prepared using a diol based Sol-Gel process, and thin films were deposited by spin coating onto Pt/Ti/$SiO_2$/Si substrates. With a single coating, final film thickness of aproximately 0.9${mu}m $ was achieved from diol-based PZT sol. Since PZT crystallized in a ferroelectric perovskite phase from an intermediate nonferroelectric pyrochlore phase, the effects of the presence of perovskite PZT seeds on the phase transformation of PZT were investigated. Seeded PZT films were prepared from the seeded PZT 1M sols in which seeds with less than 0.2${mu}m $ in size and 1wt% were dispersed in n-propanol before mixing with the PZT stock solution. The seeding effects were confirmed by the fact that the formation temperature of perovskite phase decreased by 50$^{circ}C$ with less than 1wt% seeds.