Electrically-induced strain(S) and polarization(P) for Pb(Sc1/2Nb1/2)O3-PbTiO3(1-x)PSN-xPT) crystalline solutions were studied. From the compositional dependence of S and P we could observe two maximum values at x=0.10 and x=0.425. It is considered that PSNT10(x=0.10) composition is the structural phase boundary to indicate the variable order-disorder[VOD] region. PSNT(x=0.425) composition is the morphotropic phase boundary[MPB] to indicate the rhombohedral to tetragonal phase transition. Higher S (0.437%) and P (0.3974$mu$C/$ extrm{cm}^2$) values were attained by the La substitution (5 wt%) at Pb site in the MPB composition of 57.5PSN-42.5PT.