In order to investigate the properties of the blended cement using coarsely ground blasturnace slag blended coements which were substituted from 10 to 70 wt% low Blaine slag powder (2,000 and 3,000 cm2/g) for porland cement clinker were prepared and Cal(OH)2 contents in hydrates hydration heat the fluidity and the compressive strength were measured. As the content of slag was increased the hydration heat and the early strength was decreased and the fluidity of the cement paste was improved. The heat evolution of the cement with 2,000cm2/g slag was lower than that of 3,000 cm2/g slag blended cement. Especially the heat evolution of 60wt% or above slag blended cement was similar to that of belite rich cement.