Silica glass films to utilize optical waveguides was fabricated by Aerosol Flame Deposition(AFD) method. As the amount of B2O3 increased in the sol solution of (92-x)SiO2-xB2O3-8P2O5, the thermophoretic deposition rate onto Si substrate was markedly lowered due to vaporizing out of B2O3 and P2O5 during the vaporization and reaction of the aerosol in the flame. GeO2 was added to 62SiO2-30B2O3-8P2O5 in order to control easily the refractive index of glass films. As the amount of GeO2 increased from 2 to 12 wt%, its refractive index increased from 1.4633 up to 1.4716.