The paper provides the characteristic analyses of porcelain suspension insulators. The comparisons of characteristics were made as a function of failed and unfailed insulators which had ben used in the fields. This paper also describes the failure modes occurred in the fields. The aging of cement corrosion of metal breaking of shed puncture in the head and separation of glaze are different failure modes for porcelain suspension insulators. Among these failure modes the puncture breaking and glaze problems were major concerns in this research. The cracks porosities of porcelain and micro-crystals on the graze were the causes of these failures. These results were confirmed by conducting various failure analyses.