Both the X-ray diffraction data of the normal direction in the sample orientation and the pole figure data of three reflections, (111), (200) and (220), were used to do the Rietveld refinement for the copper sheet prepared by a cold rolling process. The agreement between calculated and observed patterns was not satisfactory, which was attributed to the preferred orientation effect of the copper sheet. The Rietveld refinement for the copper sheet could be done successfully by applying the pole density of each reflection obtained from the corresponding inverse pole figure to the X-ray diffraction data of the normal direction. The R-weighted pattern, $R_{wp}$ was 12.99% and the goodness-of-fit indicator, S, was 3.68.