Silver was deposited on glass by electroless plating and electroplating. Surface properties were investigated using the AFM. Crystal structure of deposit layers was confirmed by TEM and XRD. Electroplating is performed by DC plating and pulse plating, respectively. This study resulted in followings, first, deposit of electroless plating showed fine grain and was similar to the amorphous structure. Second, electrodeposit on the electroless layer was revealed following results ; (1) more uniform layer and finer grains were obtained with increasing frequency (2) more isotropic structure was obtained with increasing frequency (3) finer grains at 25% duty cycle was obtained (4) grain size and roughness of the silver deposit was decreased with increasing frequency.