This study is the know the difference bond strength according to painting method of Opaque porcelain. Among Porcelain powder for Porcelain, Noritake powder, Bonding agent 1 class and metal are selected as Base metal alloy. And painting method of Opaque porcelain is divided by 4 groups : PG, WG, NG and DG. Also it is to manufacture 24 sheets of Specimen by 6 each every method and to measure Crack-initiation Strength of Metal-porcelain and it is to observe it by Scanning electron microscope. I come to get a conclusion as follows. 1. As for Debonding strength of every experiment groups, it showed that WS group which executed Wash bake had highest value, 44.25MPa and NG group which used Normal powder had value, 42.11MPa and DG group which used Bonding agent had value, 35.88MPa and PG group which used Paste opaque had value, 35.39MPa. 2. In four painting methods of Opaque porcelain, PG group, WG group, NG group and DG group, there is no significant difference statistically in Crack-initiation Strength. 3. As a result of observing fracture surface with Scanning electron microscope, it was showde that PG group remained a lot of particle of porcelain on the surface of metal than WG group, NG group and DG group.