In this work, the cure kinetics and rheological properties of difunctional epoxy(diglycidylether of bisphenol A, DGEBA)/polysulfone (PSF) blends were investigated using differential scanning calorimeter and rheometer. From the DSC results of the blends, the temperature of the exothermic peak and cure activation energy (E) using a half-width method were increased with increasing the PSF content to neat epoxy resin up to 30 wt%. However, a marginal decrease in the blend system was shown in E. The conversion ($alpha$) and conversion rate (d$alpha$/dt) were decreased as the content of PSF increases. Rheological properties of the blend system were investigated under isothermal condition using a rheometer. Cross-linking activation energy (E$_{c}$) was determined from the Arrhenius equation based on gel time and curing temperature. As a result, the E$_{c}$ showed a similar behavior with E which could be resulted from high viscosity of PSF and the phase separation between DGEBA and PSF.PSF.f PSF and the phase separation between DGEBA and PSF.PSF.