The effects of Dy$_2$O$_3$and Er$_2$O$_3$addition on the electromagnetic properties of Mn-Zn ferrite were investigated in the doping concentration range from 0.05 wt% to 0.25 wt%. All samples were prepared by standard fabrication of ferrite ceramics. The XRD patterns of sample were observed spinel and secondary phase. The densities of sample were showed nearly constant values. As the increased additive, electrical resistivity, initial permeability and real component of the series complex permeability increased with setting limits each other. Excess doped with Dy$_2$O$_3$ and Er$_2$O$_3$, those values decreased. The maximum electrical resistivity was observed with 0.15 we% and initial permeability was observed with 0.05 wt%. Magnetic loss decreased with additive and then increased in proportion to increased.