Amorphous $TiO_2$ thin films were deposited on glass substrates by ion beam sputtering in which the ratio of $O_2$/Ar gas used as discharged gas was varied from 0 to 2. After optical and microstructure properties and chemical composition of thin films was analyzed, antireflection coating layers were fabricated with $SiO_2$/$TiO_2$ multi-layers. Thin films deposition was performed at room temperature and ion beam voltage and ion current density for sputtering of target were fixed at 1.2 kV and 200 $mu extrm{A}/ extrm{cm}^2$, respectively. Refractive indexs of the deposited $TiO_2$films were 2.40-2.45 at a wavelength of 633 nm. $TiO_2$films had high transmission and stoichiometry when ratio of $O_2$/Ar was 1. Rms roughness of deposited $TiO_2$ film was below 7 $AA$. In excessive $O_2$ environments, however Rms roughness increased over 50 $AA$. Transmittance decreased by scattering of rough surface. Reflectance of $SiO_2$/$TiO_2$multi-layers was below 1% in visible light.