Highly homogeneous PZT powder was prepared by a partial oxalate method using chemicals of (Z $r_{0.53}$ $Ti_{0.47}$) $O_2$, Pb(N $o_3$)$_2$and (COOH)$_2$ㆍ2$H_2O$. N $b_2$ $O_{5}$ addition effect on microstructure and electrical properties of PZT ceramics was investigated. When the precursors were calcined at 71$0^{circ}C$, a single perovskite phase was obtained. After sintering at 110$0^{circ}C$, X-ray diffraction Patterns showed coexistence of rhombohedral and tetragonal phases regardless of the N $b_2$ $O_{5}$ content. As the content of N $b_2$ $O_{5}$ increased, grain size decreased but sintered density increased. The electromechanical coupling factor of kp and the piezoelectric constant of $d_{31}$ increased linearly with the content of N $b_2$ $O_{5}$, and those values reached 0.7 and -200, respectively, when 1.2 mol% of N $b_2$ $O_{5}$ is added. is added.ded.