The mechanical and electrical properties of the hot-pressed and pressureless annealed SiC-Ti $B_2$electroconductive ceramic composites were investigated as functions of the liquid additives of $Al_2$ $O_3$+ $Y_2$ $O_3$. The result of phase analysis for the SiC-Ti $B_2$ composites by XRD revealed $alpha$-SiC(6H), Ti $B_2$, and YAG(A $l_{5}$ $Y_3$ $O_{12}$ ) crystal phase. The relative density of SiC-Ti $B_2$ composites was increased with increased $Al_2$ $O_3$+ $Y_2$ $O_3$ contents. The fracture toughness showed the highest value of 6.04 Mpa $m^{frac{1}{2}}$ for composites added with l2wt% A1$_2$ $O_3$+ $Y_2$ $O_3$ additives at room temperature. The electrical resistivity showed the lowest value of 6.2$ imes$10$^{-3}$ $Omega$ㆍcm for composite added with l6wt% $Al_2$ $O_3$+ $Y_2$ $O_3$ additives at room temperature. The electrical resistivity of the SiC-Ti $B_2$ composites was all positive temperature cofficient resistance(PTCR) in the temperature ranges from $25^{circ}C$ to $700^{circ}C$.