Critical current ratio and n-value of Bi(2223)/Ag superconducting joint tape were measured as a function of uniaxial pressure. In the superconducting joint method, MM and MSM joint were used ; MM joint is direct connection of two -multi filamentary tapes, and MSM is connection of them by using a single -filamentary tape. It was observed that the critical current ratio(CCR) for jointed tapes was not dependent on the uniaxial pressure but joining methods. The n-value of jointed tapes has similar trends with that of the CCR. Especially, double MSM joint showed the highest electrical properties as 63.4-76.0%(CCR) and 3.5-5.1 (n-value). It is considered that the improvements are due to the better inter connections of multifilaments by two single filamentary tapes on both sides.