A lot of efforts have been focused on the optimization of PIT parameters for Bi-2223/Ag wire. Bi-2223 superconducting wires with 55 filaments were fabricated by stacking, drawing process. Before rolling process, round wires were pre -annealed at 760 - 820 $^{circ}C$ and low oxygen partial pressure. We confirmed that pre-annealing step was to transform Bi-2212 orthorhombic structure from Bi-2212 tetragonal structure and to reduce the formation of second phases. However Bi-2223 phases also were formed at higher than 76$0^{circ}C$ of pre-annealing temperature. The engineering critical current densities (Je) of Bi-22231Ag tapes were sintered at low oxygen partial pressure were higher than t hat of the wires sintered at air. We could achieve 6500 A/$ extrm{cm}^2$ of Je for the tape that was initially kept at slightly higher temperature than that of normal heat treatment