A Fe-Si-B-Ni amorphous alloy manufactured by one roll melt-spinning method showed the crystallization temperature difference of a maximum $10^{circ}C$ according to each lot. This temperature difference had a considerable influence on the annealing process to be conducted for obtaining the proper inductance of the alloy. The proper annealing temperature of the alloy was $480^{circ}C$ and the annealing time increased as the crystallization temperature increased. The activation energy measured by Kissinger method increased as the crystallization temperature increased. Therefore, the annealing process must be adjusted by the crystallization temperature difference of the amorphous alloy.