The polypyrrole prepared with pyrrole monomer, APS and DBSA was synthesized by chemical Polymerization at $V^{circ}C$ under atmosphere conditions. After dissolving polypyrrole powder to the chloroform including DBSA, polypyrrole film was prepared on the alumina substrate with an interdigitated electrode by using the dip-coating method. This film was soaked in methanol solvent for 1 h at room temperature and heated to $70^{circ}C$ for 4 h in $N_2$. Initial resistance was increased with the increasing humidity and decreasing temperature. The sensitivity was increased with lower humidity and decreasing temperature. The best linearity was achieved at $25^{circ}C$ and low humidity of 0%.